Aluminum Oxide Ceramic Tile as Pulley Lagging Ceramics
Detailed description
Chemshun Aluminum oxide mosaic tile are used as ceramic lining with advantage of wear-resisting, impact resisting, easy operation, etc., is ideal surface wear-resisting material of material transfer equipment in iron & steel works, thermal & power plants, mine, etc. Trades and can extend operating life of equipment effectively. It is widely used as pulley lagging ceramics in conveying engineering to protect the belts in mining industry and agriculture,etc.Pulley lagging is made through hundreds of individual ceramic lining pieces vulcanized into durable rubber plates, every applied ceramic lining tile have raised dimples for abrasion resistance. Which is best combination materials for processing .
Aluminum oxide mosaic tile characters
> High hardness with Moh's hardness 9 grade
> High abrasion and chemical resistance
> Special dumps designed for more wear resistance
> Small size in various of shape such as hexagonal, square, dimple,etc.
> Easy installation without special tool
chumshun square mosaic sheet size
| Ceramic lining pieces size |
| 17.5*17.5*5mm |
19.95*19.95*4.5*0.6 with dimples |
| 17.5*17.5*4mm |
20*30*5 with 18 pieces dimples |
| 17.5*17.5*3mm |
20*20*4 with 13 pieces dimples |
| 20*20*4/5/6mm |
20*20*8mm with 8 pieces dimples |
| 20820*12/13mm |
|
| 25*25*4mm |
|
| Note: more customized size available |
Technical data
Chemical Composition
| Al2O3 |
SiO2 |
CaO |
MgO |
Na2O |
| 92~93% |
3~6% |
1~1.6% |
0.2~0.8% |
0.1% |
Physical properties
| Specific gravity (g/cc) |
>3.60 |
| Apparent porosity (%) |
0 |
| Flexural Strength (20ºC, Mpa) |
280 |
| Compressive strength (20ºC, Mpa) |
850 |
| Rockwell hardness (HRA) |
80 |
| Vickers hardness (hv) |
1050 |
| Moh's hardness (scale) |
≥9 |
| Thermal Expansion (20-800ºC, x10-6/ºC) |
8 |
| Crystal Size (μm) |
1.3~3.0 |