Alumina Ceramic Corrosion Resistant Liner

• Standard: GB, ISO
• Application: Metallurgical Machinery, Cement Plant, Mining Machine, Thermal Power Plant, Coal Yard
• Material: Alumina Ceramic
• Type: Wear Resistant Plate
• Materials: Alumina Ceramics
• Item: Ceramics Cube in Adhesive Sticker
• Model NO.: chemshun ceramic wear resistant liner
• Size: 150*150mm, 300*300mm, 500*500mm
• Alumina Content L: 92% 95% Available
• Transport Package: Cartons Fixed on Pallet
• Specification: 150*150mm, 300*300mm, 500*500mm
• Trademark: Chemshun
• Origin: P. R. China
• HS Code: 6909120000
• Production Capacity: 5000 Tons/Year

Product Description

Alumina Ceramic Corrosion Resistant Liner

Sample brief introduction
--Item: Alumina Ceramic square cube on adhesive sticker 
--Sample size: 3mm square ceramics on adhesive sticker (150*150mm)
--Sample: Available
--Materials: 92% Al2O3 or 95% Al2O3
--Density: 3.60 or 3.68
--Moh's: 9 scale
--Application: Wear Resistant
--Finished ceramics size: 120*120mm, 150*150mm, 300*300mm, 500*500mm on Nylon Net/ silk, back/ paper back
--OEM/ODM: Acceptable
--HS Code: 6909120000

Appearance


Chumshun hexagonal tile and sheet size

Ceramic hexagonal tile size	Ceramic hexagonal mat (stick on silk /nylon net/paper) size
S12xT3mm	300*300 mm  150x150mm
S12xT6mm	300*300
S12*T13 mm	300*300
S12*T20 mm	300*300
S12*T24 mm	300*300
S12*T11 mm	300*300
Note: more customized size available

Raw Material:
The wear resistance alumina ceramic products are made from the high purity, super fine and single narrow particle high-quality grain alumina powder, which is spray-dried processing, formed by cold isostatic pressing, firing on 1520ºC~1650 ºC temperature. Subject to Al2O3 content difference, we have 92%, 95%,abrasion resistance ceramics.
 
Advantage of the material:
--High hardness
Its rockwell hardness is HRA80-90 and the Moh's hardness is up to 9 grade with is only less than diamond. And its abrasion-resistant is more better than steel and stainless steel;
--Superior Abrasion-resistance
Its abrasion-resistance is 171.5 times of Chrome steel and 260 times of manganese steel materials and as per our customers' feedback, it could prolong the use life of equipment for more than 10years under same working conditions.
--Light weight
Its density is 3.6-3.75 g/cm3, it is only half weight of steel, and could reduce the load on equipment.

Chemical Composition:

Al2O3	SiO2	CaO	MgO	Na2O
92~93%	3~6%	1~1.6%	0.2~0.8%	0.1%

 
Physical properties:

Specific gravity (g/cc)	>3.60
Apparent porosity (%)	0
Flexural Strength (20ºC, Mpa)	280
Compressive strength (20ºC, Mpa)	850
Rockwell hardness (HRA)	80
Vickers hardness (hv)	1050
Moh's hardness (scale)	≥9
Thermal Expansion (20-800ºC, x10-6/ºC)	8
Crystal Size (μm)	1.3~3.0