High Alumina Ceramic Wear Resistant Epoxy Linings with Hole
Chemshun ceramics offer standard ceramic tile and engineering ceramics for wear protection . Standard tiles is in the form of plain tile , welded tile , cone tile , pipe tile . pastable ceramic tile liner can be applied by means of plug welding , the alumina tile has a hole in the centre which a steel concave ferrel is inserted in the hole and welding takes place through the steel ferrel to weld to steel casing , this hole is then plugged with a alumina button , weld-on tile liner is perfectly fit for high temperature environment and high-speed operation equipment
Product features
1) High hardness
2) Superior abrasion resistance
3) Corrosion and chemical resistance
4) Light weight
5) Can be applied in all kinds industrial abrasion solution field
Installation site
Chemshun weldable tiles are provided with a hole though the tile, a carbon steel weld cup, and a ceramic plug for welding in pace onto a steel substrate. ceramic tile alumina content includes 92% Al2O3, 95% Al2O3.
Welding plate installation schematic diagram(welding hole and dovetail groove, arc plate)
Size available (Length*width*thickness ) :
| Pppular Sizes (Length*width*thickness ) |
| 100*100*20mm |
| 150*100*13mm, |
| 150*100*14mm, |
| 150*100*20mm, |
| 150*100*25mm, |
| 150*100*48mm, |
| 150*100*25mm |
| 150*100*48mm |
| more sizes and customized size acceptable |
Applicable Industry
1) mining industry
2) Cement industry
3) Coal handling industry
4) Steel industry
5) Port industry
6) Power plant
:
1) Chemical Composition:
| Al2O3 |
SiO2 |
CaO |
MgO |
Na2O |
| 92~93% |
3~6% |
1~1.6% |
0.2~0.8% |
0.1% |
2) Physical properties:
| Specific gravity (g/cc) |
>3.60 |
| Apparent porosity (%) |
0 |
| Flexural Strength (20ºC, Mpa) |
280 |
| Compressive strength (20ºC, Mpa) |
850 |
| Rockwell hardness (HRA) |
80 |
| Vickers hardness (hv) |
1050 |
| Moh's hardness (scale) |
≥9 |
| Thermal Expansion (20-800ºC, x10-6/ºC) |
8 |
| Crystal Size (μm) |
1.3~3.0 |