Alumina Ceramic Weldable Tile with Cap and Steel Retainer
High
alumina ceramic welded tile with hole provide excellent abrasion and impact resistance for industrial friction equipment. frequently-used as wear liner for hopper, cyclone , Chute ,separator, bunker, impellers and agitators, fan blades and fan casings, chain conveyors, mixers ect, Typical markets include grain, coal-fired power generation, mining, cement, and more. it is easily welded installation to machine no matter extremely high or low temperature working environment, also best wear resistant choice for dynamic operation equipment.
Product features
1) High hardness
2) Superior abrasion resistance
3) Corrosion and chemical resistance
4) Light weight
5) Can be applied in all kinds industrial abrasion solution field
Chemshun weldable tiles are provided with a hole though the tile, a carbon steel weld cup, and a ceramic plug for welding in pace onto a steel substrate. ceramic tile alumina content includes 92% Al2O3, 95% Al2O3.
Welding plate installation schematic diagram(welding hole and dovetail groove, arc plate)
Size available (Length*width*thickness ) :
| Pppular Sizes (Length*width*thickness ) |
| 100*100*20mm |
| 150*100*13mm, |
| 150*100*14mm, |
| 150*100*20mm, |
| 150*100*25mm, |
| 150*100*48mm, |
| 150*100*25mm |
| 150*100*48mm |
| more sizes and customized size acceptable |
:
1) Chemical Composition:
| Al2O3 |
SiO2 |
CaO |
MgO |
Na2O |
| 92~93% |
3~6% |
1~1.6% |
0.2~0.8% |
0.1% |
2) Physical properties:
| Specific gravity (g/cc) |
>3.60 |
| Apparent porosity (%) |
0 |
| Flexural Strength (20ºC, Mpa) |
280 |
| Compressive strength (20ºC, Mpa) |
850 |
| Rockwell hardness (HRA) |
80 |
| Vickers hardness (hv) |
1050 |
| Moh's hardness (scale) |
≥9 |
| Thermal Expansion (20-800ºC, x10-6/ºC) |
8 |
| Crystal Size (μm) |
1.3~3.0 |