95% Alumina Ceramic Ball for Wet Grinding & Dry Grinding
To catch the home and abroad customers' rapid increasing demand of grinding media, we develop three series of grinding balls and lining bricks with high alumina balls series: 90%, 92% and 95% alumina; Medium-alumina balls series: 68~72% alumina and Silicon carbide high alumina balls: 60~70% alumina( also called brown medium alumina balls). The customers can choose the best series that most suitable for them according to the produce demand.
Characteristics: High hardness, high density and anticorrosion.
High wear-resisting: The alumina balls' wear-resisting is higher than the common ceramic balls'. When it is working, the ball will not pollute the grinded materials, so it can keep the purity and improve the stability of grinded materials especially the ceramic glaze.
High density: The high density, high hardness and the high grinding characters save the grinding time, enlarge the smashing room. So it can improve the grinding efficiency.
High alumina grinding ball
Medium alumina grinding ball
Applied for dry grinding, wet grinding, mineral grinding, quartz grinding, lineston grinding, iron ore grinding, cement grinding, ceramics plants grinding, pigment grinding, mineral ore grinding, breaking platns.
Applied for ball mill, grinding machine, pot mill, librating mill, pebble mill, Attrition Mill, rod mill, grinding mill, grinding machine, ball grinding mill
Size: Size 1mm, 3mm, 6mm, 9mm, 13mm, 16mm, 20mm, 25mm, 30mm, 40mm, 50mm, 60mm, 70mm, 95mm
1: 90% 92% Alumina content series
A) Al2O3 ≥ 92%
B) Water absorption <0.01%
C) Bulk density ≥ 3.63 g/cm3
D) Mosh hardness: 9
E) Color: White
2: 95% High-alumina grinding ball
A) Al2O3 ≥ 95% Sio2<3.8%, others: ~3%
B) Water absorption <0.01%
C) Bulk density ≥ 3.7 g/cm3
D) Mosh hardness: 9
E) Color: White
F) self abrasion loss: <0.008%
3: Medium alumina grinding ball series:
A) Al2O3: 65%~75%
B) Bulk density ≥ 2.93g/cm3
C) Mosh hardness: 8 grade
D) self abrasion loss: 0.01
E) Color: White or brown
| Ceramic Item |
Al2O3 |
SiO2 |
Others |
| 92% ball |
92% |
<6.5% |
~2 % |
| 95% ball |
95% |
<3.6~3.7 % |
~2% |
| 68% ball |
68% |
<21.2% |
~10.18% |
B.Physical Analysis
| Item |
Alumina
Content |
Mohs hardness |
Abrasion loss
(24hours) |
Density
(g/cm3) |
Water absorption |
| 92% ball |
92% |
9 |
<0.01% |
3.6 |
<0.01% |
| 95% ball |
95% |
9 |
<0.01% |
3.74 |
<0.01% |
| 68% ball |
68% |
7-8 |
<0.03% |
3 |
<0.02% |
| Producing way ::cool-isostatic pressing , or by rolling |
C. Size :
| Diameter (mm) |
D1-3 |
D6/8/10/13/16/20/25 |
D30/40 |
D50/60/70 |
| Tolerance (±mm) |
0.5 |
1 |
2 |
3 |