Alumina Ceramic Welded Tile with Hole as Pipe Lining
High alumina ceramic welded tile with hole provide excellent abrasion and impact resistance for industrial friction equipment. It's frequently used as wear liner for hopper,cyclone,chute,separator, bunker, impellers and agitators, fan blades and fan casings, chain conveyors, mixers ect. Typical markets include grain, coal fired power generation, mining, cement, and more. It is easily welded installation to machine no matter extremely high or low temperature working environment, also best wear resistant choice for dynamic operation equipment.
Chemshun Ceramic welded tile Salient Property:
>> Excellent wear and abrasion protection property
>> Lower production and maintenance cost
>> Excellent corrosion resistance property
>> Excellent impact resistance property
>> Excellent heat resistance property
>> Easy to handle size and weight
>> Fast and safe installation
Chemshun Ceramic Advantage:
>> Afford the standard and pre-engineered tiles
>> Professional technical team to afford CAD designs
>> Professional installation team to afford install service
>> Well established process as per international standards
Installation site:
Chemshun weldable tiles are provided with a hole though the tile, a carbon steel weld cup, and a ceramic
plug for welding in pace onto a steel substrate :
>>
Welding plate installation schematic diagram(welding hole and dovetail groove, arc plate):
Size and technical date :
Size available (Length*width*thickness ) :
| Pppular Sizes (Length*width*thickness ) |
| 100*100*20mm |
| 150*100*13mm, |
| 150*100*14mm, |
| 150*100*20mm, |
| 150*100*25mm, |
| 150*100*48mm, |
| 150*100*25mm |
| 150*100*48mm |
| more sizes and customized size acceptable |
1) Chemical Composition:
| Al2O3 |
SiO2 |
CaO |
MgO |
Na2O |
| 92~93% |
3~6% |
1~1.6% |
0.2~0.8% |
0.1% |
2) Physical properties:
| Specific gravity (g/cc) |
>3.60 |
| Apparent porosity (%) |
0 |
| Flexural Strength (20ºC, Mpa) |
280 |
| Compressive strength (20ºC, Mpa) |
850 |
| Rockwell hardness (HRA) |
80 |
| Vickers hardness (hv) |
1050 |
| Moh's hardness (scale) |
≥9 |
| Thermal Expansion (20-800ºC, x10-6/ºC) |
8 |
| Crystal Size (μm) |
1.3~3.0 |