Weldable Ceramic Tiles Oxide Ceramic Wear Plate with Dovetail Groove

• Customization: Available
• Material: Aluminum
• Type: Wear Resistant Ceramic
• Model NO.: chemshun wear plate
• Item: Alumina Ceramic Wear-Resistant Products
• Alumina Content: 92% & 95%
• Density: 3.6~3.7g/Cc
• Compressive Strength: 850~1000MPa
• Size: Available and Customized Size
• Applied Equipment: Chute, Hopper, Silo, Bunker, Funnel, Pipe, Cyclone
• Application Industry: Cement, Coal, Mining, Steel, Thermal Power
• Transport Package: Carton+Pallet
• Specification: Available & Customized Size
• Trademark: Chemshun
• Origin: Pingxiang, China
• HS Code: 69091200
• Production Capacity: 5000 Ton/Year

Product Description

Weldable Ceramic Tiles Oxide Ceramic Wear Plate with Dovetail Groove

Product description
High Weld-on Dovetail ceramic tile liner with lock provide excellent abrasion and impact resistance for 
industrial friction equipment. frequently-used as wear liner for hopper, cyclone , Chute ,separator, bunker, impellers and agitators, fan blades and fan casings, chain conveyors, mixers ect, Typical markets include grain, coal-fired power generation, mining, cement, and more. it is easily welded installation to machine no matter extremely high or low temperature working environment, also best wear resistant choice for dynamic operation equipment. 

Product features
1) High hardness 
2) Superior abrasion resistance 
3) Corrosion and chemical resistance 
4) Light weight 
5) Can be applied in all kinds industrial abrasion solution field 
 

Size available (Length*width*thickness)

Pppular Sizes  (Length*width*thickness ) 

  100*100*20mm

  150*100*13mm,

  150*100*14mm, 

  150*100*20mm, 

  150*100*25mm,

  150*100*48mm,

  150*100*25mm

  150*100*48mm

more sizes and customized size acceptable

 

Technical Data

1)  Chemical Composition:

Al2O3	SiO2	CaO	MgO	Na2O
92~93%	3~6%	1~1.6%	0.2~0.8%	0.1%

 

2) Physical properties:

Specific gravity (g/cc)	>3.60
Apparent porosity (%)	0
Flexural Strength (20ºC, Mpa)	280
Compressive strength (20ºC, Mpa)	850
Rockwell hardness (HRA)	80
Vickers hardness (hv)	1050
Moh's hardness (scale)	≥9
Thermal Expansion (20-800ºC, x10-6/ºC)	8
Crystal Size (μm)	1.3~3.0