Alumina Weldable Tile Introduction :
Alumina weldable tiles liner can be applied by means of plug welding, the alumina tile has a hole in the centre which a steel concave ferrel is inserted in the hole and welding takes place through the steel ferrel to weld to steel casing, this hole is then plugged with a alumina button, weld-on tile liner is perfectly fit for high temperature environment and high-speed operation equipment.
>>> Chemshun ceramic tile liner types:
- alumina ceramic plain tile
- ceramic weldable tile liner
- ceramic curved pipe tile liner
- ceramic arc pipe tile linings
- ceramic tile with inter-locking
- alumina brick linings
- ceramic square /rectangle /hexagonal tile
- dove-tail ceramic tile liner
Material: Al2O3 92%, Al2O3 95%
>>> Ceramic tile liner sizes:
| Alumina ceramic tile popular Sizes (Length*width*thickness ) |
| 100*100*20mm (4"x4"x3/4") |
| 150*100*13mm (6"x4"x1/2") |
| 150*100*15mm (6"x4"x5/8") |
| 150*100*20mm (6"x4"x3/4") |
| 150*100*25mm (6"x4"x1") |
| 150*100*50mm (6"x4"x2") |
| 150*50*25mm (6"x4"x1") |
| 100*75*25mm (4"x3"x1") |
| 120*80*20mm |
| 228*114*25mm |
| 114*114*25mm |
More sizes and customized size acceptable.
Chemshun ceramics afford the relative weldable steel cone and ceramic rod. |
>>> Advantages:
1) Outstanding wear resistance and impact resistance, approx 10 times stronger than common pipes under same conditions.
2) Big size ceramic tubes with complicated shape molding in one have extremely ensity
3) Little gap, good integrity, smooth surface ensure the free flow of material without blocking.
4) Easy installation
5) Long service life and low maintenance cost: super wear-resistance reduce the maintenance frequency and the cost.
>>> Chemshun Advantages:
--- Tailor made engineered ceramics available
--- Accept OEM & ODM wear engineered ceramics and project
--- Provide professional industrial wear consult and solution
--- Accept small and big quantity order
--- Delivery fast
>>> Chemical Composition:
| Al2O3 |
SiO2 |
CaO |
MgO |
Na2O |
| 92~93% |
3~6% |
1~1.6% |
0.2~0.8% |
0.1% |
>>> Physical properties:
| Specific gravity (g/cc) |
>3.60 |
| Apparent porosity (%) |
0 |
| Flexural Strength (20ºC, Mpa) |
280 |
| Compressive strength (20ºC, Mpa) |
850 |
| Rockwell hardness (HRA) |
80 |
| Vickers hardness (hv) |
1050 |
| Moh's hardness (scale) |
≥9 |
| Thermal Expansion (20-800ºC, x10-6/ºC) |
8 |
| Crystal Size (μm) |
1.3~3.0 |