Zirconium Balls as Grinding Media From Industry Ceramic Manufacturer
Chemshun TZP beads have high fracture toughness and nice impact resistant that causes no break under high speed impact
The TZP beads have 30-50 times higher wear-resistance as glass beads,
5times higher as Zirconium Silicate beads and 6-8 times higher as Al2O3 beads
Because of the high density and excellent grinding efficiency of our TZP beads , they greatly apply to grinding and dispersing high viscosity materials
Popular size :Ø0.1,Ø0.2,Ø0.4~0.8,Ø0.8~1.0,Ø1.0~Ø1.2,Ø1.2~Ø1.4,Ø0.4~Ø1.6,Ø1.6~Ø1.8,Ø1.8~Ø2,Ø2~Ø2.5
Chemshun Y-TZP zirconia grinding balls technical data :
| Properties |
Unit |
Data |
| Composition |
wt% |
94.6% ZrO2 5.2% Y2O3 |
| Specific density |
g/cm3 |
5.95-6.0 |
| Moh's hardness |
grade |
> 9.0 |
| Elastic modulus |
Gpa |
205 |
| Thermal conductivity |
W/m.k |
3 |
| Crushing load |
Kn |
>20 (Dia 7 mm) |
| Fracture toughness |
Mpa m1/2 |
7-10 |
| Grain size |
µm |
<0.5 |
Thermal expansion
Coefficient (20-400 ºC) |
10*10-6/ºC(20-400) |
11 |
Size range of beads
Size range of cylinder |
Mm
Mm |
0.1--55
6---40 |
Other Alumina ceramic grinding ball introduction :
This product are featured by high density and hardness, low wear lost, corrosion-resistance etc. They are the perfect high-efficient grinding media for milling glaze/frit, pigment, ceramic materials, and various mine ore powder, they are using ceramics, cements, paints, refractories, inorganic mineral powders etc...
Applied for dry grinding , wet grinding ,mineral grinding , quartz grinding , lineston grinding , iron ore grinding , cement grinding , ceramics plants grinding , pigment grinding , mineral ore grinding , breaking platns .
Applied for ball mill,grinding machine , pot mill , librating mill , pebble mill , Attrition Mill,rod mill , grinding mill , grinding machine , ball grinding mill
Size:1mm, 3mm, 6mm, 9mm, 13mm, 16mm, 20mm, 25mm, 30mm , 40mm, 50mm, 60mm, 70mm,95mm
Other grinding ball like alumina grinding ball itroduced :
1: 92% 95% 68% Alumina content series
A) Al2O3 ≥ 92%
B) Water absorption <0.01%
C) Bulk density ≥ 3.63 g/cm3
D) Mosh hardness: 9
E) Color: White
2: 95% High-alumina grinding ball
A) Al2O3 ≥ 95% Sio2<3.8%, others:~3%
B) Water absorption <0.01%
C) Bulk density ≥ 3.7 g/cm3
D) Mosh hardness: 9
E) Color: White
F) self abrasion loss : <0.008%
3: 68% Medium alumina grinding ball series :
A) Al2O3 : 65%~75%
B) Bulk density ≥ 2.93g/cm3
C) Mosh hardness: 8 grade
D) self abrasion loss :0.01
E) Color : white or brown
Ceramic Item |
Al2O3 |
SiO2 |
Others |
| 92% ball |
92% |
<6.5% |
~2 % |
| 95% ball |
95% |
<3.6~3.7 % |
~2% |
| 68% ball |
68% |
<21.2% |
~10.18% |
B.Physical Analysis
| Item |
Alumina
Content |
Mohs hardness |
Abrasion loss
(24hours) |
Density
(g/cm3) |
Water absorption |
| 92% ball |
92% |
9 |
<0.01% |
3.6 |
<0.01% |
| 95% ball |
95% |
9 |
<0.01% |
3.74 |
<0.01% |
| 68% ball |
68% |
7-8 |
<0.03% |
3 |
<0.02% |
| Producing way ::cool-isostatic pressing , or by rolling |
C : Size :
| Diameter (mm) |
D1-3 |
D6/8/10/13/16/20/25 |
D30/40 |
D50/60/70 |
| Tolerance (±mm) |
0.5 |
1 |
2 |
3 |
More Abrasion ceramics products : abrasion ceramics , Alumina ceramics , wear
resistant ceramics , alumina pipe liner , ceramic tube , alumina cylinder pipe , wear resistant alumina
plate , abrasion ceramic tile , abrasive alumina sheet , friction plain tile , abrasion weldable tile , rubber