High Alumina Ceramic Hex Tile Mat as Ceramic Pulley Lagging
light duty ceramic sheet and ceramic wear plates offer extremely long wear life in applications with sliding wear. The thickness and the low weight make these products ideal in applications where weight and space are limiting factors.The low friction, smooth surface prevents material build-up in low inclination installations. The square ceramic tiles make it possible to bend the sheeting which makes it the perfect protection for both con-cave and convex surfaces
>>> Product character :
--- High hardness with Moh's hardness 9 grade
----High abrasion and chemical resistance
----Easy installation by epoxy resin glue water
----Easy mending if someone hex tile drop off
---- Various of alumina ceramic hex sheet size available
>>> Property :
| Properties |
Unit |
CHEMSHUN 92 |
CHEMSHUN 95 |
| Al2O3 |
% |
92 |
95 |
| Density |
g/cm3 |
3.6 |
3.65 |
| Moh's Hardness |
Grade |
9 |
9 |
| Products |
Size in mm (L*W*T) or (S*T) |
| Ceramic square tile |
10*10*2~10, 17.5*17.5*2~15, 20*20*2~20, 33*33*5~25 etc |
| Ceramic hexagonal tile |
6*3~6, 11*3~25, 12*3~25,19.05*3~25 |
| Ceramic block |
32*32*32, 40*40*40 |
| Hex/square tile mats |
150*150, 300*300, 500*500 |
| Material of mats |
Paper, nylon mesh, acetate cloth etc. |
>>> Application :
-- mining industry
-- Cement industry
-- Coal handling industry
-- Steel industry
-- Port industry
-- Power plant
>>> Chemical Composition:
| Al2O3 |
SiO2 |
CaO |
MgO |
Na2O |
| 92~93% |
3~6% |
1~1.6% |
0.2~0.8% |
0.1% |
Physical properties:
| Specific gravity (g/cc) |
>3.60 |
| Apparent porosity (%) |
0 |
| Flexural Strength (20ºC, Mpa) |
280 |
| Compressive strength (20ºC, Mpa) |
850 |
| Rockwell hardness (HRA) |
80 |
| Vickers hardness (hv) |
1050 |
| Moh's hardness (scale) |
≥9 |
| Thermal Expansion (20-800ºC, x10-6/ºC) |
8 |
| Crystal Size (μm) |
1.3~3.0 |