Abrasive Resistant Ceramic Pipe Tile Liner for Industrial Pipeline System
Product Description
Chemshun ceramic pipe tile liner includes alumina curved plate and trapezoidal taper tile liner. Which combined into a circle with customer required size. Compared with integrated pipe liner, Chemshun ceramic pipe tile is an excellent wear protection and wear solution cost effective ceramic material.
Chemshun ceramic pipe tile liner with wear resistant, impact resisting, easy to operation is ideal surface abrasion resistant material of bulk material transfer equipment in iron & steel works, thermal & power plants, port and terminals, cement, etc. Alumina Ceramic curved plate and trapezoidal taper tile fabricated as pipe linings for its radian and angle specially designed, best choice of cyclone, bend pipe, orifice, transition, inner cone equipments. Chemshun can offer engineering ceramics and pre-fabricated ceramics lined equipment for customer's abrasion resistant project drawings. Chemshun can produce ceramic tile alumina content including 92% Al2O3, 95% Al2O3.
Product characters
1) Compared with integrated pipe liner, ceramic pipe tile liner is more cost effective in purchasing cost
2) Easy to be installed in equipment
3) Easy to repair when any piece ceramics damaged
4) Any size can be combined freely compared with integrated pipe
Size available (Length*width*thickness)
| Chemshun ceramic pipe liner tile normal Size |
| 150*100/95.63*50mm, |
150*100/95.34*50mm |
150*50/46*25 mm, |
| 157*100*48/35 mm, |
100/68*102/70*50 mm |
125/62.2*102*50mm |
| 80*23.9/22.1*20 mm |
80*25.5/22.7*10mm |
80*27.3/25.9*10 mm |
| 80*27.4/25.73*8mm |
80*28.5/27.3*10mm |
25.4*25.4/24.4*12.7mm |
| 97*50/48*15 mm |
100*60/59.44*15mm |
|
| Note: more sizes and customized size acceptable |
Technical Data Sheet
1): Chemshun wear Ceramic Chemical Composition:
| Al2O3 |
SiO2 |
CaO |
MgO |
Na2O |
| 92~93% |
3~6% |
1~1.6% |
0.2~0.8% |
0.1 |
2): Chemshun ceramics pipe lining tiles Physical properties:
| Specific gravity (g/cc) |
>3.60 |
| Apparent porosity (%) |
0 |
| Flexural Strength (20ºC, Mpa) |
280 |
| Compressive strength (20ºC, Mpa) |
850 |
| Rockwell hardness (HRA) |
80 |
| Vickers hardness (hv) |
1050 |
| Moh's hardness (scale) |
≥9 |
| Thermal Expansion (20-800ºC, x10-6/ºC) |
8 |
| Crystal Size (μm) |
1.3~3.0 |