Abrasion and Impact Resistant Weldable Ceramic Tile Liner
1: Chemshun advantage:
----- We can afford the standard and pre-engineered tiles;
----- We can afford the fabricated and lined equipment (finished product) according to customer
requirement.
----- We have professional technical team to afford the CAD design drawings for the pre-engineered tiles.
----- We have professional installation team to afford install service.
------ We have good process as per international standards.
2: Wledable ceramic tile liner description :
Chemshun abrasion resistant materials is made by ISO pressed alumina . Which is a extremely dense ceramic material that has remarkable resistance to both sliding and impact abrasion. the exceptional thoughness and durability of alumina has made it the recognised standard for long term economic lining in industrial equipment subject to high wear.weldable ceramic tile liner is applied where high heat , impact or corrosion, the weldable system permits use of weldable ceramic tile liner to temperatures in excess of 550 centi-degree, this weld-on tiles are supplied with a tapered hole,metal insert and an alumina cap.
3: weldable ceramic tile liner advantage :
-- High hardness
-- Superior abrasion resistance
-- Corrosion and chemical resistance
-- Light weight with low density
-- Can be applied in all kinds industrial abrasion solution field
4: Chemshun weldable ceramic tile liner size :
Alumina ceramic weldable tile popular Sizes (Length*width*thickness ) |
100*100*20mm (4"x4"x3/4") |
150*100*13mm (6"x4"x1/2") |
150*100*15mm (6"x4"x5/8") |
150*100*20mm (6"x4"x3/4") |
150*100*25mm (6"x4"x1") |
150*100*50mm (6"x4"x2") |
150*50*25mm (6"x4"x1") |
100*75*25mm (4"x3"x1") |
120*80*20mm |
228*114*25mm |
114*114*25mm |
More sizes and customized size acceptable. Chemshun ceramics afford the relative weldable steel cone and ceramic rod. |
5: Technical Data :
1) Chemical data :
Al2O3 |
SiO2 |
CaO |
MgO |
Na2O |
92~93% |
3~6% |
1~1.6% |
0.2~0.8% |
0.1% |
2) Physical data :
Specific gravity (g/cc) |
>3.60 |
Apparent porosity (%) |
0 |
Flexural Strength (20ºC, Mpa) |
280 |
Compressive strength (20ºC, Mpa) |
850 |
Rockwell hardness (HRA) |
80 |
Vickers hardness (hv) |
1050 |
Moh's hardness (scale) |
≥9 |
Thermal Expansion (20-800ºC, x10-6/ºC) |
8 |
Crystal Size (μm) |
1.3~3.0 |