Aluminum Oxide Ceramic Mosaic Tile as Pulley Lagging Ceramics
<<<< Aluminum oxide ceramic mosaic tile as pulley lagging ceramics Introduction:
Chemshun Aluminum oxide ceramic mosaic tile are used as ceramic lining with advantage of wear-resisting, impact resisting, easy operation, etc., is ideal surface wear-resisting material of material transfer equipment in iron & steel works, thermal & power plants, mine, etc. Trades and can extend operating life of equipment effectively. It is widely used as pulley lagging ceramics in conveying engineering to protect the belts in mining industry and agriculture,etc.Pulley lagging is made through hundreds of individual ceramic lining pieces vulcanized into durable rubber plates, every applied ceramic lining tile have raised dimples for abrasion resistance. Which is best combination materials for processing .
<<<<Aluminum oxide mosaic tile characters:
-- High hardness with Moh's hardness 9 grade
-- High abrasion and chemical resistance
-- Special dumps designed for more wear resistance
-- Small size in various of shape such as hexagonal, square, dimple,etc.
-- Easy installation without special tool
<<<<chumshun square mosaic sheet size:
Ceramic lining pieces size |
17.5*17.5*5mm |
19.95*19.95*4.5*0.6 with dimples |
17.5*17.5*4mm |
20*30*5 with 18 pieces dimples |
17.5*17.5*3mm |
20*20*4 with 13 pieces dimples |
20*20*4/5/6mm |
20*20*8mm with 8 pieces dimples |
20820*12/13mm |
|
25*25*4mm |
|
Note: more customized size available |
<<<< Application industry:
--- Used to be a part of ceramic rubber plate for anti-wear and anti-impact lining.
--- Used as component of pulley lagging
--- Used as tile mats widely lining in conveying engineering to protect the belts in mining, power plant, steel plant and agriculture,etc
<<<< Aluminum oxide ceramic mosaic tile technical data:
S.No. |
Attributes |
Unit |
CHEMSHUN 92 I |
CHEMSHUN92 II |
1 |
Alumina Content |
% |
92 |
92 |
2 |
Density |
g/cc |
≥3.60 |
≥3.60 |
3 |
Color |
- |
White |
White |
4 |
Water Absorption |
% |
<0.01 |
<0.01 |
5 |
Flexural Strength |
Mpa |
270 |
300 |
6 |
Moh's Density |
Grade |
9 |
9 |
7 |
Rock Well Hardness |
HRA |
80 |
85 |
8 |
Vickers Hardness(HV5) |
Kg/mm2 |
1000 |
1150 |
9 |
Fracture Toughness (Min) |
MPa.m1/2 |
3-4 |
3-4 |
10 |
Compressive strength |
Mpa |
850 |
850 |
11 |
Thermal Expansion Coefficient (25-1000ºC) |
1x10-6/ºC |
8.0 |
7.6 |
12 |
Maximum operation temperature |
ºC |
1450 |
1450 |