Alumina Ceramic Block Cubes for Rubber Vulcanization

• Application: Industrial Ceramic
• Material: Alumina Ceramic
• Type: Ceramic Parts
• Item: Alumina Block
• Materials: Alumina Ceramic
• Alumina Content: 92% 95%
• Model NO.: CHEMSHUN CERAMICS
• Size: 40*40*40; 40*40*20
• Color: White
• Character: High Purity/Hardness, Abrasion/Wear-Resistant
• Firing Temperature: 1550~1680degree Centigrade
• Apparent Porosity: 0
• OEM: Accept
• Transport Package: Carton+Pallets
• Specification: 40*40*40; 40*40*20; 40*20*25; 30*30*25; 30*15*25
• Trademark: chemshun
• Origin: China
• HS Code: 69091200
• Production Capacity: 5000ton/Year

Product Description

Alumina Ceramic Block Cubes for Rubber Vulcanization

>>> Description :
Inter-locking alumina wear ceramic block is much different from wear plain tile, pipe liner ,weld-on tile liner. It is specially designed with groove and tongues , which help ceramic liner to get stuck during application. What's more , alumina wear ceramic block is with much thickness ,it is can be used to resist toughest applications with very high material flow containing coarse material. Which can void ceramic liner surface crack and waste materials handling . Chemshun inter-locking alumina wear ceramic block can be widely used for vulcanization in rubber sheet . Or directly bonded in equipment for wear protection
 

Alumina ceramic block popular Sizes  (Length*width*thickness )

40*40*25 mm

40*20*25 mm

30*30*25 mm

30*15*25 mm

40*40*40 mm

40*40*50 mm

40*20*50 mm

40*40*10 mm

38*38*38 mm

32*32*32 mm

32*32*16 mm

More sizes and customized size acceptable.
All alumina ceramic cube with tongues and grooves.

>>> Character:
--  Special Shape with grooves or tongues
--  Designed for special engineering
--  Excellent connectivity
--  Easy to pack and installation for using





Chemshun Ceramics wear-resistant product application industries:
- Mining
- Mineral processing (mineral beneficiation)
- Power generation
- Cement
- Petro-Chemical Refining and Production
- Coal washery
- Steel
- Defense (personal & vehicle armour).
 

Al2O3	SiO2	CaO	MgO	Na2O
92~93%	3~6%	1~1.6%	0.2~0.8%	0.1%

Physical properties:

Specific gravity (g/cc)	>3.60
Apparent porosity (%)	0
Flexural Strength (20 degree centigrade, Mpa)	334
Compressive strength (20degree centigrade, Mpa)	1770
Rockwell hardness (kg/mm 2 )	918
Vickers hardness (hv)	>750
Moh's hardness (scale)	≥9
Thermal Expansion (20-800degree centigrade, x10-6/degree centigrade)	8.30
Crystal Size (μm)	1.3~3.0