Pulley Lagging Ceramic Liner as Industry Conveyor Pulley Lagging
Pulley Lagging Ceramic Liner detailed description
With the characteristics of easy construction .pulley lagging ceramic liners are broadly applied on transfer points of a conveyor, they are not only suitable for chutes,feeding pipes, elbow and straight pipes, but also for emergency maintenance such as the repairs of performation on rubber and the sheel of pulleys .raised ceramic mosaic tile are designed to increase the coefficient of friction between the lagging and the belt . they will provide a longer service life for the pulley and belt. while enabling the system to run at a lower tension, reducing power consumption
Pulley lagging ceramic liner characters
-- High hardness with Moh's hardness 9 grade
-- High abrasion and chemical resistance
-- Special dumps designed for more wear resistance
-- Light weight with various sizes
chumshun square mosaic sheet size
| Ceramic lining pieces size |
| 17.5*17.5*5mm |
19.95*19.95*4.5*0.6 with dimples |
| 17.5*17.5*4mm |
20*30*5 with 18 pieces dimples |
| 17.5*17.5*3mm |
20*20*4 with 13 pieces dimples |
| 20*20*4/5/6mm |
20*20*8mm with 8 pieces dimples |
| 20820*12/13mm |
|
| 25*25*4mm |
|
| Note: more customized size available |
Pulley lagging ceramic liner aplication industry
--mining industry
--Cement industry
--Coal handling industry
--Steel industry
--Port industry
--Power plant
Technical data
1) :Chemical Composition:
| Al2O3 |
SiO2 |
CaO |
MgO |
Na2O |
| 92~93% |
3~6% |
1~1.6% |
0.2~0.8% |
0.1% |
Physical properties:
| Specific gravity (g/cc) |
>3.60 |
| Apparent porosity (%) |
0 |
| Flexural Strength (20ºC, Mpa) |
280 |
| Compressive strength (20ºC, Mpa) |
850 |
| Rockwell hardness (HRA) |
80 |
| Vickers hardness (hv) |
1050 |
| Moh's hardness (scale) |
≥9 |
| Thermal Expansion (20-800ºC, x10-6/ºC) |
8 |
| Crystal Size (μm) |
1.3~3.0 |