High Wear Resistance Raised Ceramic Mosaic Tile Vulcanized in Pulley Lagging

• Customized: Customized
• Application: Papermaking, Food, Construction, Ocean, Aerospace, Aviation, Electronics, Metallurgy, Pharmacy, Salt, Chemical, Petroleum
• Certification: API, ISO, BSI, CE
• Material: Alumina Ceramic
• Feature: Wear Resistant
• Corrosion Rate: 0.01-0.1
• Model NO.: ceramic mosaic tile
• Raw Material: Alumina Powder
• Size: Customized
• Shape Way: Plain,Weldable,Curved,Trapezoidal,Dimple
• Character: High Purity/Hardness, Abrasion-Resistant
• Color: White
• Firing Temperature: 1550~1680degree Centigrade
• Apparent Porosity: 0
• OEM: Accept
• Transport Package: Paper Carton+Pallet
• Specification: 20*20, 31*31, 40*40, 35*35
• Trademark: Chemshun
• Origin: Pingxiang, China
• HS Code: 69091900
• Production Capacity: 50000ton/Year

Product Description

High Wear Resistance Raised Ceramic Mosaic Tile Vulcanized in Pulley Lagging

Product Description
With the characteristics of easy construction . ceramic liners are broadly applied on transfer points of a conveyor, they are not only suitable for chutes,feeding pipes, elbow and straight pipes, but also for emergency maintenance such as the repairs of performation on rubber and the sheel of pulleys .raised ceramic mosaic tile are designed to increase the coefficient of friction between the lagging and the belt . they will provide a longer service life for the pulley and belt. while enabling the system to run at a lower tension, reducing power consumption 

Alumina ceramic cylinder characters
--  High hardness with Moh's hardness 9 grade 
--  High abrasion and chemical resistance 
--  Special dumps designed for more wear resistance 
--  Light weight with various sizes 

Sizes

Ceramic lining pieces size
17.5*17.5*5mm	19.95*19.95*4.5*0.6 with dimples
17.5*17.5*4mm	20*30*5 with 18 pieces dimples
17.5*17.5*3mm	20*20*4 with 13 pieces dimples
20*20*4/5/6mm	20*20*8mm with 8 pieces dimples
20820*12/13mm
25*25*4mm
Note: more customized size available

Tenical Data Sheet

Specific gravity (g/cc)	>3.60
Apparent porosity (%)	0
Flexural Strength (20ºC, Mpa)	270
Compressive strength (20ºC, Mpa)	850
Rockwell hardness (HRA)	80
Vickers hardness (hv)	1000
Moh's hardness (scale)	≥9
Thermal Expansion (20-800ºC, x10-6/ºC)	8
Crystal Size (μm)	1.3~3.0
Fracture Toughness (Mpa.M^1/2)	3-4
Maximum Operation Temperature(ºC)	1450