92% 95% Al2O3 Alumina Ceramics Grinding Media Ball for Ball Mill

• Material: Alumina
• Content: >90%
• Usage: Machinery, Grind
• Processing Type: Rolling Type
• Size: Middle
• Color: White
• Model NO.: Chemshun Ceramics
• Customized: Customized
• Transport Package: Woven Bags/Pallets
• Specification: 20/25/30/40/50/60/70
• Trademark: Pingxiang Chemshun Ceramics
• Origin: China
• HS Code: 69091200
• Production Capacity: 10000/Tons/Year

Product Description

92% 95% Al2O3 alumina Ceramics Grinding Media Ball For Ball mill

Product Description
This product are featured by high density and hardness, low wear lost, corrosion-resistance etc. They are the perfect high-efficient grinding media for milling glaze/frit, pigment, ceramic materials, and various mine ore powder, they are using ceramics, cements, paints, refractories, inorganic mineral powders etc...

Appearance:


Applied for dry grinding , wet grinding ,mineral grinding ,  quartz grinding ,  lineston grinding ,  iron ore grinding , cement grinding , ceramics plants grinding , pigment grinding , mineral ore grinding , breaking platns .

Applied for ball mill,grinding machine , pot mill , librating mill , pebble mill , Attrition Mill,rod mill , grinding mill , grinding machine , ball grinding mill

Size:1mm, 3mm, 6mm, 9mm, 13mm, 16mm, 20mm, 25mm, 30mm , 40mm, 50mm, 60mm, 70mm,95mm

1: 92%  Alumina content series
A) Al2O3 ≥ 92%
B) Water absorption <0.01%
C) Bulk density ≥ 3.63 g/cm3
D) Mosh hardness: 9
E) Color: White

2: 95% High-alumina grinding ball
A) Al2O3 ≥ 95%  Sio2<3.8%, others:~3%
B) Water absorption <0.01%
C) Bulk density ≥ 3.7 g/cm3
D) Mosh hardness: 9
E) Color: White
F) self abrasion loss : <0.008%

3: 68% Medium alumina grinding ball series :
A) Al2O3 : 65%~75%
B) Bulk density ≥ 2.93g/cm3
C) Mosh hardness: 8 grade
D) self abrasion loss :0.01
E) Color : white or brown

92% Alumina grinding ball chemical and physical introduction :

Items	Proportion	Items	Proportion
Al2O3	92%	SiO2	<6.5%
others	~2%

 

Items	Proportion	Items	Proportion
Hardness: Mohr's	9	self Abrasion Loss (24hour)	<0.01%
Density(g/cm3)	3.6g/cm3	Water Absorption	<0.01%
Color	White	Ball method	By cool isostatic-pressing Or by rolling

95% Alumina ball chemical and physical introduction:

Items	Proportion	Items	Proportion
Al2O3	95%	SiO2	<3%
others	~2%

       

Items	Proportion	Items	Proportion
Hardness: Mohr's	9	self Abrasion Loss (24hour)	<0.01%
Density(g/cm3)	3.74g/cm3	Water Absorption	<0.01%
Color	White	Ball method	By cool isostatic-pressing Or by rolling

68% Alumina ball chemical and physical introduction:

Items	Proportion	Items	Proportion
Al2O3	68.62%	SiO2	21.2%
others	~10.18%

    

Items	Proportion	Items	Proportion
Hardness: Mohr's	7-8	self Abrasion Loss (24hour)	<0.03%
Density(g/cm3)	3.g/cm3	Water Absorption	<0.1%
Color	creamy white	Ball method	By cool isostatic-pressing Or by rolling