Alumina Ceramic Weladble Plate as Abrasion Resistant Materials
Product Description
High alumina ceramic welded tile with hole provide excellent abrasion and impact resistance for industrial friction equipment. frequently-used as wear liner for hopper, cyclone, chute, separator, bunker, impellers and agitators, fan blades and fan casings, chain conveyors, mixers, ect. Typical markets include grain, coal-fired power generation, mining, cement, and more. it is easily welded installation to machine no matter extremely high or low temperature working environment, also best wear resistant choice for dynamic operation equipment.
Product features
1) High hardness
2) Superior abrasion resistance
3) Corrosion and chemical resistance
4) Light weight
5) Can be applied in all kinds industrial abrasion solution field
Chemshun weldable tiles are provided with a hole though the tile, a carbon steel weld cup, and a ceramic plug
for welding in pace onto a steel substrate, ceramic tile alumina content includes 92% Al2O3, 95% Al2O3.
Size available (Length*width*thickness)
| Pppular Sizes (Length*width*thickness ) |
| 100*100*20mm |
| 150*100*13mm, |
| 150*100*14mm, |
| 150*100*20mm, |
| 150*100*25mm, |
| 150*100*48mm, |
| 150*100*25mm |
| 150*100*48mm |
| more sizes and customized size acceptable |
Applicable Industry
1) Mining industry
2) Cement industry
3) Coal handling industry
4) Steel industry
5) Port industry
6) Power plant
Technical Data Sheet
Chemical Composition:
| Al2O3 |
SiO2 |
CaO |
MgO |
Na2O |
| 92~93% |
3~6% |
1~1.6% |
0.2~0.8% |
0.1% |
Physical properties:
| Specific gravity (g/cc) |
>3.60 |
| Apparent porosity (%) |
0 |
| Flexural Strength (20ºC, Mpa) |
280 |
| Compressive strength (20ºC, Mpa) |
850 |
| Rockwell hardness (HRA) |
80 |
| Vickers hardness (hv) |
1050 |
| Moh's hardness (scale) |
≥9 |
| Thermal Expansion (20-800ºC, x10-6/ºC) |
8 |
| Crystal Size (μm) |
1.3~3.0 |