Wear Resistant Alumina Ceramic Lined Pipe for Slurry, Powder Removal

• Application: Refractory, Industrial Ceramic, Metallurgical
• Material: Alumina Ceramic
• Type: Ceramic Plates
• Standard: GB, ISO
• Item: Alumina Ceramic Wear-Resistant Liner
• Alumina Content: 92% & 95%
• Model NO.: Chemshun Ceramics
• Density: 3.6~3.7 G/Cc
• Size: Available and Customized Size
• Characters: High Wear Resistant, High Density
• Transport Package: Carton+Pallet
• Specification: Available and Customized size
• Trademark: Chemshun
• Origin: Pingxiang, China
• HS Code: 69091200
• Production Capacity: 5000ton/Year

Product Description

Wear Resistant Alumina Ceramic Lined Pipe for Slurry, Powder Removal


Alumina ceramic lined pipeline characters:
>  Long lifetime and maintenance free operation
>  NO operation interruption or production losses
>  NO contamination of the conveyed materials due to abrasion, mixture or oxidation
>  Physiologically harmless, suitable for food products
> Smooth surface to achieve good flowability and to avoid plugs
>  No spilled material to clean up

Application pictures:
Chemshun ceramics produce Wear resistant:
Alumina ceramic lined pipe equipment  on site installation service



Wear resistant alumina ceramic lined pipe

 

Chumshun pipe size available:

 

Chemshun ceramics offer ceramic pipe liner and ceramic pipe tile liner for pipe
Use ceramic pipe	ID:10mm~500mm	Thickness and length according to customer's needs
Use pipe tile liner	Any pipe size available	Thickness :13mm , 25mm, 50mm etc
Note:More sizes and customized size acceptable

Application industry:

>  Mining industry 
>  Cement industry 
>  Coal handling industry 
>  Steel industry 
>  Port industry 
>  Power plant 

Technical data:

1): Chemical Composition:

Al2O3	SiO2	CaO	MgO	Na2O
92~93%	3~6%	1~1.6%	0.2~0.8%	0.1%

 
2): Physical properties:

Specific gravity (g/cc)	>3.60
Apparent porosity (%)	0
Flexural Strength (20ºC, Mpa)	280
Compressive strength (20ºC, Mpa)	850
Rockwell hardness (HRA)	80
Vickers hardness (hv)	1050
Moh's hardness (scale)	≥9
Thermal Expansion (20-800ºC, x10-6/ºC)	8
Crystal Size (μm)	1.3~3.0