Ceramic Wear Resistant Tiles for Stackers and Reclaimers
High Ceramic Wear Resistant Tiles with hole provide excellent abrasion and impact resistance for industrial
friction equipment.frequently-used as wear liner for hopper, cyclone , Chute ,separator, bunker, impellers and
agitators, fan blades and fan casings, chain conveyors, mixers, stackers and reclaimers, ect. Typical markets
include grain, coal-fired power generation, mining, cement, and more. it is easily welded installation to machine no matter extremely high or low temperature working environment, also best wear resistant choice for dynamic operation equipment.
Product features:
1) High hardness
2) Superior abrasion resistance
3) Corrosion and chemical resistance
4) Light weight
5) Can be applied in all kinds industrial abrasion solution field
Size available (Length*width*thickness ) :
| Pppular Sizes (Length*width*thickness ) |
| 100*100*20mm |
| 150*100*13mm, |
| 150*100*14mm, |
| 150*100*20mm, |
| 150*100*25mm, |
| 150*100*48mm, |
| 150*100*25mm |
| 150*100*48mm |
| More sizes and customized size acceptable |
Applicable Industry:
1) Mining industry
2) Cement industry
3) Coal handling industry
4) Steel industry
5) Port industry
6) Power plant
1) Chemical Composition:
| Al2O3 |
SiO2 |
CaO |
MgO |
Na2O |
| 92~93% |
3~6% |
1~1.6% |
0.2~0.8% |
0.1% |
2) Physical properties:
| Specific gravity (g/cc) |
>3.60 |
| Apparent porosity (%) |
0 |
| Flexural Strength (20ºC, Mpa) |
280 |
| Compressive strength (20ºC, Mpa) |
850 |
| Rockwell hardness (HRA) |
80 |
| Vickers hardness (hv) |
1050 |
| Moh's hardness (scale) |
≥9 |
| Thermal Expansion (20-800ºC, x10-6/ºC) |
8 |
| Crystal Size (μm) |
1.3~3.0 |