Chemshun Wear Resistant Alumina Zirconia Balls for Grinding Mill
Chemshun TZP beads have high fracture toughness and nice impact resistant that causes no break under high speed impact.
The TZP beads have 30-50 times higher wear-resistance as glass beads, 5 times higher as Zirconium Silicate beads and 6-8 times higher as Al2O3 beads.
Because of the high density and excellent grinding efficiency of our TZP beads , they greatly apply to grinding and dispersing high viscosity materials.
Popular size: Ø0.1, Ø0.2, Ø0.4~0.8, Ø0.8~1.0, Ø1.0~Ø1.2, Ø1.2~Ø1.4, Ø0.4~Ø1.6, Ø1.6~Ø1.8, Ø1.8~Ø2, Ø2~Ø2.5
Chemshun Y-TZP zirconia grinding balls technical data:
Properties |
Unit |
Data |
Composition |
wt% |
94.6% ZrO2 5.2% Y2O3 |
Specific density |
g/cm3 |
5.95-6.0 |
Moh's hardness |
grade |
> 9.0 |
Elastic modulus |
Gpa |
205 |
Thermal conductivity |
W/m.k |
3 |
Crushing load |
Kn |
>20 (Dia 7 mm) |
Fracture toughness |
Mpa m1/2 |
7-10 |
Grain size |
µm |
<0.5 |
Thermal expansion Coefficient (20-400 ºC) |
10*10-6/ºC(20-400) |
11 |
Size range of beads Size range of cylinder |
Mm Mm |
0.1--55 6---40 |
Other Alumina ceramic grinding ball introduction :
This product are featured by high density and hardness, low wear lost, corrosion-resistance etc. They are the perfect high-efficient grinding media for milling glaze/frit, pigment, ceramic materials, and various mine ore powder, they are using ceramics, cements, paints, refractories, inorganic mineral powders, etc.
Applied for dry grinding, wet grinding ,mineral grinding, quartz grinding, lineston grinding, iron ore grinding, cement grinding, ceramics plants grinding, pigment grinding, mineral ore grinding, breaking platns.
Applied for ball mill, grinding machine, pot mill, librating mill, pebble mill, Attrition Mill,rod mill, grinding mill, grinding machine, ball grinding mill.
Size: 1mm, 3mm, 6mm, 9mm, 13mm, 16mm, 20mm, 25mm, 30mm , 40mm, 50mm, 60mm, 70mm, 95mm
Other grinding ball like alumina grinding ball introduced:
1: 92% 95% 68% Alumina content series
A) Al2O3 ≥ 92%
B) Water absorption <0.01%
C) Bulk density ≥ 3.63 g/cm3
D) Mosh hardness: 9
E) Color: White
2: 95% High-alumina grinding ball
A) Al2O3 ≥ 95% Sio2<3.8%, others:~3%
B) Water absorption <0.01%
C) Bulk density ≥ 3.7 g/cm3
D) Mosh hardness: 9
E) Color: White
F) Self abrasion loss: <0.008%
3: 68% Medium alumina grinding ball series :
A) Al2O3: 65%~75%
B) Bulk density ≥ 2.93g/cm3
C) Mosh hardness: 8 grade
D) Self abrasion loss: 0.01
E) Color: white or brown
Ceramic Item |
Al2O3 |
SiO2 |
Others |
92% ball |
92% |
<6.5% |
~2 % |
95% ball |
95% |
<3.6~3.7 % |
~2% |
68% ball |
68% |
<21.2% |
~10.18% |
B. Physical Analysis
Item |
Alumina Content |
Mohs hardness |
Abrasion loss (24hours) |
Density (g/cm3) |
Water absorption |
92% ball |
92% |
9 |
<0.01% |
3.6 |
<0.01% |
95% ball |
95% |
9 |
<0.01% |
3.74 |
<0.01% |
68% ball |
68% |
7-8 |
<0.03% |
3 |
<0.02% |
Producing way: cool-isostatic pressing, or by rolling |
C. Size
Diameter (mm) |
D1-3 |
D6/8/10/13/16/20/25 |
D30/40 |
D50/60/70 |
Tolerance (±mm) |
0.5 |
1 |
2 |
3 |